Abstract:
Employing atomic layer deposition, we have grown p-type epitaxial undoped and N-doped' anatase TiO2(001) thin films on c-axis Al2O3 substrate. From X-ray diffraction and transmission electron microscopy studies, crystallographic relationships-between the film and the substrate are found to be (001)(TiO2)/(0001)(Al2O3) and [(1) over bar 10](TiO2)//[01 (1) over bar0]Al2O3. N-doping in TiO2 thin films enhances the hole concentration and mobility. The optical band gap of anatase TiO2 (3.23 eV) decreases to 3.07 eV upon N-doping. The epitaxial films exhibit room-temperature ferromagnetism and photoresponse. A TiO2-based homojunction diode was fabricated with rectification from the p-n junction formed between N-doped p-TiO2 and n-TiO2.