Coordination Polymers and Hybrid Networks of Different Dimensionalities Formed by Metal Sulfites

Abstract

In our effort to explore the use of the sulfite ion to design hybrid and open-framework materials, we have been able to prepare, under hydrothermal conditions, zero-dimensional [Zn(C12H8N2)(SO3)]center dot 2H(2)O, I (a = 7.5737(5) angstrom, b = 10.3969(6) angstrom, c = 10.3986(6) angstrom, alpha = 64.172(1)degrees, beta = 69.395(1)degrees, gamma = 79.333(1)degrees, Z = 2, and space group P (1) over bar), one-dimensional [Zn-2(C12H8N2)(SO3)(2)(H2O)], II (a = 8.0247(3) angstrom, b = 9.4962(3) angstrom, c = 10.2740(2) A, alpha = 81.070(1)degrees, beta = 80.438(1)degrees, gamma = 75.66(5)degrees, Z = 2, and space group P (1) over bar), two-dimensional [Zn-2(C10H8N2)(SO3)(2)]center dot H2O, III (a = 16.6062(1) angstrom, b = 4.7935(1) angstrom, c = 19.2721(5) angstrom, beta = 100.674(2)degrees, Z = 4, and space group C2/c), and three-dimensional [Zn-4(C6H12N2)(SO3)(4)(H2O)(4)], IV (a = 11.0793(3) angstrom, c = 8.8246(3) angstrom, Z = 2, and space group P42nm), of which the last three are coordination polymers. A hybrid open-framework sulfite-sulfate of the composition [C2H10N2][Nd(SO3)(SO4)(H2O)](2), V (a = 9.0880(3) angstrom, b = 6.9429(2) angstrom, c = 13.0805(5) A, beta = 91.551(2)degrees, Z = 2, and space group P2(1)/c), with a layered structure containing metal-oxygen-metal bonds has also been described.